ABSTRACT The impulse excitation, as non-destructive technique, allows to determine the elastic constants of materials by means of measurement of natural frequency of vibration of bars in different modes, excited by an impact in a point. In this work, the Young’s modulus of copper, aluminum and copper-based alloys samples was determined. The measurements were performed using different vibration modes: flexural in supported bars, and longitudinal. As a first step, the Young´s modulus of a sample was determined using different modes, finding consistency in results. On the other hand, the variation of the Young´s modulus was determined as a function of the temperature and microstructural parameters such as grain size. The capabilities and disadvantages of using the impulse excitation technique as a low-cost alternative in the field of research in metals and alloys are analyzed.

RESUMEN La excitación por impulso como técnica no destructiva para el estudio de materiales permite determinar las constantes elásticas de los mismos por intermedio de la medición de la frecuencia natural de vibración de barras en diferentes modos y excitadas mediante un impacto puntual. En este trabajo se determinó el módulo de Young en muestras de cobre, aluminio y aleaciones de base cobre. Las mediciones se realizaron usando distintos modos de vibración: flexión en una barra apoyada y longitudinal. Como primer paso se determinó el módulo de Young de una muestra usando diferentes modos, encontrando consistencia en los resultados. Por otro lado, se determinó la variación del módulo de Young en función de la temperatura y parámetros microestructurales como el tamaño de grano. Se analizan las capacidades y desventajas del uso de la técnica de excitación por impulso como una alternativa de bajo costo en el ámbito de la investigación en metales y aleaciones.

In this work, epoxy/poly-3-hydroxybutyrate (PHB) blends in two different proportions, 90/10 and 85/15, were studied. For this purpose, the samples were submitted to 80ºC and 120ºC for the curing process of epoxy. The phase separation and the crystallization were analyzed using optical microscopy and differential scanning calorimetry. Likewise, the lamellar structure of PHB was characterized using small angle X-ray scattering. Significant differences between the two proportions studied were found; while the 90/10 sample presents miscibility, the 85/15 sample indicates a phase separation. Besides, the lamellar structure of PHB is affected due to the epoxy, mainly in the 90/10 sample. The results were analyzed on the basis of the competition between crystallization and phase separation processes.

En este trabajo se estudiaron mezclas epoxy/poli-3-hidroxibutirato (PHB) en dos proporciones distintas 90/10 y 85/15. Para ello se prepararon muestras sometiéndolas a temperaturas de 80 ºC y 120 ºC, a efectos de producir el curado del epoxy. Se analizó la separación de fases y la cristalización del PHB mediante microscopía óptica y calorimetría diferencial de barrido. Asimismo la estructura lamelar del PHB se caracterizó mediante dispersión de rayos X de bajo ángulo. Se encontraron diferencias significativas entre las dos proporciones estudiadas; mientras que la muestra 90/10 presenta miscibilidad, la muestra 85/15 indica una separación de fases. Asimismo se encontró que, sobre todo para la muestra 90/10, el epoxy afecta considerablemente la estructura lamelar del PHB. Los resultados se analizaron en términos de la competencia entre los procesos de cristalización y separación de fases.